Xytron™ G4080HR

40% Glass Reinforced, Flame Retardant, Hydrolysis resistant

Back to results

General Information

Xytron™ is a high performance plastic compound of Envalior, which is based on PPS (polyphenylene sulphide).
Xytron™ offers extremely good chemical resistance, dimensional stability, intrinsic flame retardancy and high stiffness.
Because of its outstanding properties, Xytron™ contributes to an excellent performance in many different applications.
Special features
  • Hydrolysis resistant or enhanced hydrolytic stability
General Document
Regulatory Affairs
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-04-25
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Processing technology
Injection Molding
Design challenge
Degradation & Stability | Chemical stability
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.2
%
Molding shrinkage (normal)
0.5
%

Mechanical properties

Tensile modulus
15000
MPa
Tensile modulus (-40°C)
15000
MPa
Tensile modulus (90°C)
12000
MPa
Tensile modulus (120°C)
6300
MPa
Tensile modulus (160°C)
4400
MPa
Tensile modulus (200°C)
3500
MPa
Stress at break
190
MPa
Stress at break (-40°C)
240
MPa
Stress at break (90°C)
125
MPa
Stress at break (120°C)
85
MPa
Stress at break (160°C)
62
MPa
Stress at break (200°C)
50
MPa
Strain at break
2
%
Strain at break (-40°C)
2
%
Strain at break (90°C)
2.75
%
Strain at break (120°C)
4.5
%
Strain at break (160°C)
5.1
%
Strain at break (200°C)
5.8
%
Flexural modulus
14000
MPa
Flexural modulus (120°C)
5800
MPa
Flexural modulus (160°C)
4400
MPa
Flexural modulus (200°C)
3900
MPa
Flexural strength
290
MPa
Flexural strength (120°C)
130
MPa
Flexural strength (160°C)
95
MPa
Flexural strength (200°C)
75
MPa
Charpy impact strength (+23°C)
60
kJ/m²
Charpy impact strength (-30°C)
70
kJ/m²
Charpy notched impact strength (+23°C)
10.5
kJ/m²
Charpy notched impact strength (-30°C)
10
kJ/m²
Izod impact strength (+23°C)
55
kJ/m²
Izod notched impact strength (+23°C)
11.5
kJ/m²
Izod notched impact strength (-40°C)
10.5
kJ/m²
Weldline strength at thickness 1
80
MPa
Weldline strain at thickness 1
0.8
%
Thickness tested (1)
4
mm
Rockwell hardness, R scale
120
-
Rockwell hardness, M scale
100
-

Thermal properties

Melting temperature (10°C/min)
280
°C
Glass transition temperature (10°C/min)
90
°C
Temp. of deflection under load (1.80 MPa)
265
°C
Temp. of deflection under load (0.45 MPa)
280
°C
Temp. of deflection under load (8.00 MPa)
185
°C
Coeff. of linear therm. expansion (parallel)
0.15
E-4/°C
Coeff. of linear therm. expansion (normal)
0.4
E-4/°C
Coef. of lin. therm expansion, parallel, above Tg
0.15
E-4/°C
Coef. of lin. therm expansion, normal, above Tg
1.1
E-4/°C

Electrical properties

Relative permittivity (1GHz)
4
-
Relative permittivity (5GHz)
4
-
Dissipation factor (1GHz)
35
E-4
Dissipation factor (5GHz)
55
E-4
Volume resistivity
>1E13
Ohm*m
Surface resistivity
>1E15
Ohm
Electric strength
31
kV/mm
Comparative tracking index
175
V

Other properties

Water absorption in water at 23°C after 24h
0.04
%
Humidity absorption
0.04
%
Density
1650
kg/m³

Diagrams

Applications

Hydrogen fuel cells

Industry
Automotive
Material
  • •} Fuel cell systems need to use materials that are pure. If not, ion leaching will occur which will poison the catalyst & clog the membrane, lead to life time & efficiency drop of fuel cell system
  • •} Moreover, material with excellent hydrolytic and heat aging resistance is highly favorable to ensure its life time performance. Xytron™, our high-performance PPS compound, offers the high purity and superior mechanical performance needed to achieve the industry’s lowest ion leaching performance at temperatures up to 120°C, and highest hydrolytic and chemical resistance. This enables OEMs to develop long-lasting, highly efficient PEMFCs that lower the cost per kilometer and total cost of ownership for end users.
}
More information

Thermal management modules

Industry
Automotive
Material
  • •} Broad portfolio of advanced material solutions for thermal management
  • •} Extensive global thermal management application development expertise
  • •} Xytron™ PPS offers best-in-class hydrolysis resistance and weld line strength
}
More information

Water pump impellers

Industry
Automotive
Material
  • •} Broad portfolio of advanced material solutions for thermal management
  • •} Extensive global thermal management application development expertise
  • •} Xytron™ PPS offers best-in-class hydrolysis resistance and weld line strength
}
More information