Stanyl® TS271A1

Aramid fibre reinforced, Wear and Friction Modified

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Product
Stanyl® TS271A1 is a aramid-reinforced friction-modified high heat polyamide that offers extremely low abrasion for gear & bushing applications
Special features
Regulatory Affairs
Processing technology
Injection Molding
Design challenge
Wear & Friction
Automotive OEM
HYUNDAI KIA
OEM Specification
MS-211-66-(2018)

Rheological properties

Molding shrinkage [parallel]
1.5
%
Molding shrinkage [normal]
1.5
%

Mechanical properties

Tensile modulus
2800
MPa
Stress at break
90
MPa
Strain at break
13
%
Flexural modulus
3100
MPa
Flexural strength
125
MPa
Charpy notched impact strength (+23°C)
6
kJ/m²

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
200
°C
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (1) tested)
0.75
mm

Other properties

Water absorption
10.5
%
Water absorption in water at 23°C after 24h
3
%
Humidity absorption
2.9
%
Density
1270
kg/m³