Stanyl® TE248F6

30% Glass Reinforced, Heat Stabilized, UV Stabilized

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
General Document
Processing technology
Injection Molding

Rheological properties

Molding shrinkage (parallel)
0.5
%
Molding shrinkage (normal)
1.3
%
Spiral flow length 1.0 mm 800 bar
100
mm
Spiral flow length 1.0 mm 900 bar
110
mm
Spiral flow length 1.0 mm 1000 bar
120
mm

Mechanical properties

Tensile modulus
10000
MPa
Tensile modulus (120°C)
5300
MPa
Tensile modulus (160°C)
4750
MPa
Stress at break
210
MPa
Stress at break (120°C)
115
MPa
Stress at break (160°C)
100
MPa
Strain at break
3.7
%
Strain at break (120°C)
7.5
%
Strain at break (160°C)
8
%
Izod notched impact strength (+23°C)
12
kJ/m²

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
290
°C
Temp. of deflection under load (0.45 MPa)
290
°C
Vicat softening temperature (50°C/h 50N)
290
°C
Coeff. of linear therm. expansion (parallel)
0.25
E-4/°C
Coeff. of linear therm. expansion (normal)
0.6
E-4/°C
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
HB
class
Thickness tested
3
mm
UL recognition
Yes
-
Oxygen index
22
%
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (2) tested)
3
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (2) tested)
3
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (2) tested)
3
mm

Electrical properties

Relative permittivity (100Hz)
4.4
-
Relative permittivity (1 MHz)
4
-
Relative permittivity (1GHz)
3.6
-
Dissipation factor (100 Hz)
80
E-4
Dissipation factor (1 MHz)
230
E-4
Dissipation factor (1GHz)
300
E-4
Volume resistivity
1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
35
kV/mm
Comparative tracking index
500
V

Other properties

Humidity absorption
2.6
%
Density
1410
kg/m³

Material specific properties

Viscosity number
145
cm³/g

Diagrams

Applications

Audio Jack Connectors

Industry
Electronics
  • •} Cost-effective
  • •} High flowability
  • •} Low moisture absorption
  • •} Flame retardant
}

Reflow connectors

Industry
Electronics
  • •} Cost-effective
  • •} High flowability
  • •} Enable thin-wall designs
  • •} Low moisture absorption
  • •} Flame retardant
}