Stanyl® TE200S6

30% Glass Beads Reinforced, Heat Stabilized, Low Warpage

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
Regulatory Affairs
Processing technology
Injection Molding
Automotive OEM
FORD
OEM Specification
WSK-M4D916-A

Rheological properties

Molding shrinkage [parallel]
1.3
%
Molding shrinkage [normal]
1.7
%

Mechanical properties

Tensile modulus
4700
MPa
Tensile modulus (120°C)
1000
MPa
Tensile modulus (160°C)
900
MPa
Tensile modulus (180°C)
800
MPa
Tensile modulus (200°C)
740
MPa
Stress at break
90
MPa
Stress at break (120°C)
45
MPa
Stress at break (160°C)
35
MPa
Stress at break (180°C)
32
MPa
Stress at break (200°C)
30
MPa
Strain at break
4.5
%
Strain at break (120°C)
30
%
Strain at break (160°C)
29
%
Strain at break (180°C)
28
%
Strain at break (200°C)
27
%
Izod notched impact strength (+23°C)
4
kJ/m²

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
235
°C

Electrical properties

Relative permittivity (100Hz)
4.4
-
Relative permittivity (1 MHz)
4
-
Relative permittivity (1GHz)
3.6
-
Dissipation factor (100 Hz)
80
E-4
Dissipation factor (1 MHz)
230
E-4
Dissipation factor (1GHz)
300
E-4
Volume resistivity
1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
35
kV/mm

Other properties

Water absorption
9.5
%
Water absorption in water at 23°C after 24h
2.65
%
Humidity absorption
2.6
%
Density
1410
kg/m³

Material specific properties

Viscosity number
145
cm³/g

Diagrams