Stanyl® TE200F6-FC

30% Glass Reinforced, Heat Stabilized, Food Contact Quality

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
Regulatory Affairs

Rheological properties

Molding shrinkage [parallel]
0.5
%
Molding shrinkage [normal]
1.3
%
Spiral flow length 1.0 mm 800 bar
100
mm
Spiral flow length 1.0 mm 900 bar
110
mm
Spiral flow length 1.0 mm 1000 bar
120
mm

Mechanical properties

Tensile modulus
10000
MPa
Tensile modulus (-40°C)
10200
MPa
Tensile modulus (120°C)
5300
MPa
Tensile modulus (160°C)
4750
MPa
Tensile modulus (180°C)
4550
MPa
Tensile modulus (200°C)
4300
MPa
Tensile modulus, low thickness
10000
MPa
Tens. Mod. (Thickness tested)
1
mm
Stress at break
210
MPa
Stress at break (-40°C)
250
MPa
Stress at break (120°C)
115
MPa
Stress at break (160°C)
100
MPa
Stress at break (180°C)
95
MPa
Stress at break (200°C)
90
MPa
Stress at break, at low thickness
210
MPa
Stress at break (Thickness tested)
1
mm
Strain at break
3.7
%
Strain at break (-40°C)
3.5
%
Strain at break (120°C)
7.5
%
Strain at break (160°C)
8
%
Strain at break (180°C)
8
%
Strain at break (200°C)
8
%
Strain at break, at low thickness
3.8
%
Strain at break (Thickness tested)
1
mm
Flexural modulus
9500
MPa
Flexural modulus (120°C)
5100
MPa
Flexural modulus (160°C)
4900
MPa
Flexural strength
300
MPa
Flexural strength (120°C)
160
MPa
Flexural strength (160°C)
130
MPa
Charpy impact strength (+23°C)
80
kJ/m²
Charpy impact strength (-30°C)
65
kJ/m²
Charpy notched impact strength (+23°C)
12
kJ/m²
Charpy notched impact strength (-30°C)
11
kJ/m²
Izod notched impact strength (+23°C)
12
kJ/m²
Izod notched impact strength (-40°C)
11
kJ/m²
Weldline strength at thickness 1
100
MPa
Weldline strain at thickness 1
1.5
%
Thickness tested (1)
4
mm

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
290
°C
Temp. of deflection under load (0.45 MPa)
290
°C
Vicat softening temperature (50°C/h 50N)
290
°C
Coeff. of linear therm. expansion (parallel)
0.25
E-4/°C
Coeff. of linear therm. expansion (normal)
0.6
E-4/°C
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
HB
class
Thickness tested
3
mm
UL recognition
Yes
-
Oxygen index
22
%
Glow Wire Flammability Index GWFI
925
°C
GWFI (Thickness (1) tested)
3
mm
Glow Wire Flammability Index GWFI
675
°C
GWFI (Thickness (2) tested)
0.75
mm
Glow Wire Ignition Temperature GWIT
725
°C
GWIT (Thickness (1) tested)
3
mm
Glow Wire Ignition Temperature GWIT
700
°C
GWIT (Thickness (2) tested)
0.75
mm
Thermal Index 2500 hrs
171
°C
Thermal Index 5000 hrs
159
°C
Thermal Index 10000 hrs
147
°C
Thermal Index 20000 hrs
137
°C

Electrical properties

Relative permittivity (100Hz)
4.4
-
Relative permittivity (1 MHz)
4
-
Relative permittivity (1GHz)
3.6
-
Dissipation factor (100 Hz)
80
E-4
Dissipation factor (1 MHz)
230
E-4
Dissipation factor (1GHz)
300
E-4
Volume resistivity
1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
35
kV/mm
Comparative tracking index
500
V

Other properties

Water absorption
9.5
%
Water absorption in water at 23°C after 24h
2.65
%
Humidity absorption
2.6
%
Density
1410
kg/m³

Material specific properties

Viscosity number
145
cm³/g

Rheological calculation properties

Density of melt
1280
kg/m³
Thermal conductivity of melt
0.28
W/(m K)
Spec. heat capacity melt
2430
J/(kg K)
Eff. thermal diffusivity
9.02E-8
m²/s

Diagrams

Applications

Kitchen appliance gears, dishwasher proof

Industry
Consumer goods
  • •} Heat-stabilized
  • •} Superior heat resistance, design stiffness, wear and friction, and process flow qualities
  • •} Ideal for extremely high-performance applications
  • •} Outperforms PPA, PA6T, PA9T, and often PPS and LCP
}

Kitchen utensils

Industry
Consumer goods
  • •} Application requirements
  • •} Stiffness at high temperature
  • •} Long term heat resistance
  • •} Dishwasher proof
  • •} Food contact
  • •} Good aesthetics
  • •} Thermal shock resistance
  • •} Water cooled tooling capable & high productivity
  • •} Material properties
  • •} HDT- A ForTii 305-320°C
  • •} HDT-A Stanyl 290°C HDT-A
  • •} EcoPaXX 215°C
  • •} Approved food contact regulation including EU 2011-10 FDA
}

Panhandle

Industry
Consumer goods
Application requirements Stiffness at high temperature Long term heat resistance Dishwasher proof Food contact Good esthetics Thermal shock resistance Water cooled tooling capable & high productivity Material properties HDT-A > 290 to 320°C UL 94 HB rating Approved food contact regulation including EU 2011-10, FDA}

Pipe Fittings

Industry
Building & construction
  • •} Akulon has better surface appearance
  • •} Stanyl solves wear and friction issues
  • •} EcoPaXX has the lowest carbon footprint amongst common polyamides
  • •} Xytron offers extremely good chemical resistance
}

Spatulas and Kitchenware

Industry
Consumer goods
Stanyl® PA46 and Akulon® PA66 are reliable solutions for spatulas and other kitchenware. Stanyl PA46 offers much higher melting temperature and HDT than PA66, and both materials have significantly higher melting temperature resistance than PP and PA6. Also, Stanyl TE200F6-FC and EcoPaXX® Q-KG6-FC are food-approved.}