Stanyl® MC51
35% Glass Reinforced, High Flow, Flame Retardant (halogen- phosphorous-free)
General Information
Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
- Good or high flow
- Phosphorous free
General Document
Processing technology
Injection Molding
Injection Molding
Design challenge
Flame Retardancy | Halogen free
Flame Retardancy | Halogen free
Rheological properties
Molding shrinkage (parallel)
0.4
%
ISO 294-4
Molding shrinkage (normal)
1.1
%
ISO 294-4
Spiral flow length 1.0 mm 1000 bar
230
mm
-
Mechanical properties
Tensile modulus
12500
MPa
ISO 527-1/-2
Tensile modulus, low thickness
12500
MPa
ISO 527-1/-2
Tens. Mod. (Thickness tested)
1
mm
ISO 527-1/-2
Stress at break
185
MPa
ISO 527-1/-2
Stress at break, at low thickness
200
MPa
ISO 527-1/-2
Stress at break (Thickness tested)
1
mm
ISO 527-1/-2
Strain at break
1.9
%
ISO 527-1/-2
Strain at break, at low thickness
2.3
%
ISO 527-1/-2
Strain at break (Thickness tested)
1
mm
ISO 527-1/-2
Flexural modulus
12000
MPa
ISO 178
Flexural strength
270
MPa
ISO 178
Charpy impact strength (+23°C)
60
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
12
kJ/m²
ISO 179/1eA
Weldline strength at thickness 1
75
MPa
ISO 527-1/-2
Weldline strain at thickness 1
0.7
%
ISO 527-1/-2
Thickness tested (1)
1
mm
ISO 527-1/-2
Thermal properties
Melting temperature (10°C/min)
280
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
280
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
285
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.4
E-4/°C
ASTM D696
Coeff. of linear therm. expansion (normal)
0.45
E-4/°C
ASTM D696
Burning Behav. at thickness h
V-2
class
IEC 60695-11-10
Thickness tested
0.85
mm
IEC 60695-11-10
UL recognition
Yes
-
IEC 60695-11-10
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
3
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
825
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
3
mm
IEC 60695-2-13
Electrical properties
Volume resistivity
1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
Ohm
IEC 62631-3-2
Comparative tracking index
425
V
IEC 60112
Other properties
Water absorption
6.7
%
Sim. to ISO 62
Water absorption in water at 23°C after 24h
1.7
%
ISO 62
Humidity absorption
2.3
%
Sim. to ISO 62
Density
1470
kg/m³
ISO 1183