Stanyl® HFX33S

20% Glass Reinforced, High Flow, Halogen free and free of red phosphorous

Back to results

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Product
Stanyl® HFX33S is an electro-friendly & halogen-free flame-retarded high heat polyamide that offers an excellent combination of high CTI, flow and weld-line strength. HFX-grades are often used in connectors such as USB type C.
Special features
  • Good or high flow
  • Phosphorous free
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2023-11-16
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Yellow Card
Processing technology
Injection Molding
Design challenge
Downsizing & Miniaturization
Flame Retardancy | Halogen free
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.4
%
Molding shrinkage (normal)
1.5
%
Spiral flow length 1.0 mm 800 bar
165
mm
Spiral flow length 1.0 mm 900 bar
180
mm
Spiral flow length 1.0 mm 1000 bar
200
mm

Mechanical properties

Tensile modulus
7800
MPa
Tensile modulus (120°C)
4000
MPa
Tensile modulus (160°C)
3500
MPa
Tensile modulus, low thickness
7600
MPa
Tens. Mod. (Thickness tested)
1
mm
Stress at break
120
MPa
Stress at break (120°C)
67
MPa
Stress at break (160°C)
58
MPa
Stress at break, at low thickness
115
MPa
Stress at break (Thickness tested)
1
mm
Strain at break
2.8
%
Strain at break (120°C)
5.1
%
Strain at break (160°C)
5.9
%
Strain at break, at low thickness
2.9
%
Strain at break (Thickness tested)
1
mm
Flexural modulus
7000
MPa
Flexural modulus (120°C)
4000
MPa
Flexural modulus (160°C)
3600
MPa
Flexural strength
170
MPa
Flexural strength (120°C)
95
MPa
Flexural strength (160°C)
85
MPa
Charpy impact strength (+23°C)
37
kJ/m²
Charpy notched impact strength (+23°C)
7.5
kJ/m²
Weldline strength at thickness 1
48
MPa
Weldline strain at thickness 1
0.83
%
Thickness tested (1)
4
mm
Weldline strength at thickness 2
56
MPa
Weldline strain at thickness 2
0.93
%
Thickness tested (2)
1
mm

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
276
°C
Temp. of deflection under load (0.45 MPa)
284
°C
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
Thickness tested
3
mm
UL recognition
Yes
-

Electrical properties

Relative permittivity (1GHz)
3.5
-
Dissipation factor (1GHz)
100
E-4
Electric strength
30
kV/mm
Comparative tracking index
500
V

Other properties

Water absorption in water at 23°C after 24h
2.2
%
Humidity absorption
2.8
%
Density
1370
kg/m³

Diagrams

Applications

E-Motors for Power Tools

Industry
Consumer goods
Material
  • •} Current e-motor applications are packed tight with little to no room to gain additional power or improve efficiency. With Stanyl® PA46, you can mold thinner walls (i.e., lamina stack insulation) down to .25 mm or less, allowing more room for copper windings or thicker gauge to maximize torque potential and reduce resistance.
  • •} At high loads, e-motors generate substantial heat. Temperatures can easily exceed 150°C (302°F), resulting in mechanical failures. Stanyl® PA46 offers excellent high temperature mechanical performance with a heat deflection temperature of 290°C (554°F) and a continuous use temperature of 170°C (338°F).
  • •} The superior flow and high crystallinity of Stanyl® PA46 results in strong and flexible weld lines, improving manufacturing yield by eliminating process scrap in rotors and stators.
}
More information

USB-C Connectors

Industry
Electronics
Material
  • •} Glass-reinforced
  • •} Provides up to 50% more wear resistance compared to other high temperature polyamides
  • •} Enables thinner wall designs
  • •} Halogen and red phosphorous-free grades are available
}
More information