Stanyl® Diablo OCD2305 BM

Glass Reinforced, Heat Stabilized, Blow Molding Grade

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
Regulatory Affairs
Processing technology
Blow Molding, Injection Molding
Design challenge
Degradation & Stability | Thermo-oxidative stability
Automotive OEM
CALLOUT, FIAT CHRYSLER, RENAULT
OEM Specification
ASTM D6779 PA0620G25 A43480 Z1Z6Z7
FCA-MS50017(MS-DB-41)-CPN5219-(2017-02)
PMR (2019-02)

Rheological properties

Melt volume-flow rate
32
cm³/10min
Temperature
295
°C
Load
21.6
kg

Mechanical properties

Tensile modulus
8500
MPa
Tensile modulus (-40°C)
8800
MPa
Tensile modulus (100°C)
3600
MPa
Tensile modulus (150°C)
3000
MPa
Tensile modulus (180°C)
2600
MPa
Tensile modulus (200°C)
2200
MPa
Tensile modulus (210°C)
2000
MPa
Stress at break
165
MPa
Stress at break (-40°C)
220
MPa
Stress at break (100°C)
90
MPa
Stress at break (150°C)
75
MPa
Stress at break (180°C)
65
MPa
Stress at break (200°C)
55
MPa
Stress at break (210°C)
52
MPa
Strain at break
3.4
%
Strain at break (-40°C)
3.3
%
Strain at break (150°C)
15
%
Strain at break (180°C)
18
%
Strain at break (200°C)
19
%
Strain at break (210°C)
21
%
Flexural modulus
9000
MPa
Flexural strength
250
MPa
Charpy notched impact strength (+23°C)
13
kJ/m²
Charpy notched impact strength (-30°C)
7
kJ/m²

Thermal properties

Melting temperature (10°C/min)
284
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
240
°C
Temp. of deflection under load (0.45 MPa)
275
°C
Coeff. of linear therm. expansion (parallel)
0.25
E-4/°C
Coeff. of linear therm. expansion (normal)
0.9
E-4/°C

Electrical properties

Volume resistivity
>1E13
Ohm*m

Other properties

Density
1330
kg/m³

Diagrams

Applications

Hot Charged Air Ducts

Industry
Automotive
  • <ul> <li>Stanyl® PA46, Stanyl® Diablo PA46, Akulon® Diablo PA and Arnitel® HT TPC allow for light weight solutions as compared to metal or rubber or alternative plastics (Stanyl® is 10% lighter than PPS)</li> <li>Stanyl® PA46, Stanyl® Diablo PA46, Akulon® Diablo PA and Arnitel® HT TPC allow for cost effective solutions (Stanyl lowers system cost up to 20% versus metal)</li> <li>Stanyl® PA46, Stanyl® Diablo PA46, Akulon® Diablo PA and Arnitel® HT TPC allow for reliable solutions (Stanyl® Diablo is long term resistant up to 230 ˚C, Akulon® Diablo ca be used around 200 ˚C) and Arnitel® HT is ideal as single part solution for flexible hot charge ducts.</li> </ul>