Stanyl® Diablo OCD2300 BK27021

50% Glass Reinforced, Heat Stabilized

Back to results

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2023-11-16
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Processing technology
Injection Molding
Design challenge
Degradation & Stability | Thermo-oxidative stability
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.4
%
Molding shrinkage (normal)
0.9
%

Mechanical properties

Tensile modulus
17000
MPa
Tensile modulus (120°C)
6700
MPa
Tensile modulus (160°C)
5800
MPa
Tensile modulus (180°C)
5300
MPa
Tensile modulus (200°C)
4300
MPa
Tensile modulus (210°C)
3600
MPa
Stress at break
240
MPa
Stress at break (120°C)
110
MPa
Stress at break (160°C)
85
MPa
Stress at break (180°C)
75
MPa
Stress at break (200°C)
60
MPa
Stress at break (210°C)
55
MPa
Strain at break
2.4
%
Strain at break (120°C)
7.5
%
Strain at break (160°C)
8.5
%
Strain at break (180°C)
9
%
Strain at break (200°C)
9.5
%
Strain at break (210°C)
11
%
Flexural modulus
17000
MPa
Flexural modulus (120°C)
6900
MPa
Flexural modulus (160°C)
6100
MPa
Flexural modulus (180°C)
5600
MPa
Flexural modulus (200°C)
4500
MPa
Flexural modulus (210°C)
4100
MPa
Flexural strength
370
MPa
Flexural strength (120°C)
145
MPa
Flexural strength (160°C)
110
MPa
Flexural strength (180°C)
95
MPa
Flexural strength (200°C)
75
MPa
Flexural strength (210°C)
65
MPa
Charpy impact strength (+23°C)
95
kJ/m²
Charpy impact strength (-30°C)
80
kJ/m²
Charpy notched impact strength (+23°C)
17
kJ/m²
Charpy notched impact strength (-30°C)
14
kJ/m²

Thermal properties

Melting temperature (10°C/min)
275
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
260
°C
Temp. of deflection under load (0.45 MPa)
270
°C
Coeff. of linear therm. expansion (parallel)
0.25
E-4/°C
Coeff. of linear therm. expansion (normal)
0.4
E-4/°C

Other properties

Water absorption
5.4
%
Water absorption in water at 23°C after 24h
2.2
%
Humidity absorption
2.2
%
Density
1620
kg/m³