Nylatron® GS-51

32% Glass Reinforced, MoS2 Lubricated

Back to results

General Information

Special features
  • Lubricated
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2023-11-16
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • CALIFORNIA PROPOSITION 65 (NDS)2024-01-02
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Yellow Card
Processing technology
Injection Molding
Automotive OEM
FIAT CHRYSLER, GM
OEM Specification
FCA-MS50017(MS-DB-41)-CPN4198-(2017-02)
GMW18101P-PA66-GF35
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.4
%
Molding shrinkage (normal)
1.2
%

Mechanical properties

Tensile modulus
10500
MPa
Stress at break
185
MPa
Strain at break
3
%
Flexural modulus
9200
MPa
Charpy notched impact strength (+23°C)
10
kJ/m²
Charpy notched impact strength (-30°C)
7
kJ/m²
Izod notched impact strength (+23°C)
9.5
kJ/m²

Thermal properties

Melting temperature (10°C/min)
260
°C
Glass transition temperature (10°C/min)
60
°C
Temp. of deflection under load (1.80 MPa)
250
°C
Temp. of deflection under load (0.45 MPa)
260
°C
Coeff. of linear therm. expansion (parallel)
0.2
E-4/°C
Coeff. of linear therm. expansion (normal)
0.7
E-4/°C
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (1) tested)
1.5
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
1.5
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (1) tested)
1.5
mm

Other properties

Water absorption
6
%
Humidity absorption
1.6
%
Density
1400
kg/m³