Novamid® ID 1030-CF10

3D printing grade, 10% Carbon Reinforced

General Information

This is a filament grade - not available for sale as granules.
Novamid® ID 1030-CF10 can 3D-print high-performance and durable structural end-use parts, making 3D printing technology a viable option for demanding automotive structural applications that require robust performance at elevated temperatures. With a carbon fiber loading of just 10%, Novamid® ID 1030-CF10 prints parts with properties close to what is usually achievable only by injection molding. It can be printed at the same speeds as unreinforced plastics, while achieving considerably better strength and toughness.
Special features
Regulatory Affairs
Processing technology
3D printing

Mechanical properties

Tensile modulus
7570
MPa
Yield stress
110
MPa
Yield strain
2.8
%
Stress at break
110
MPa
Strain at break
3
%

Thermal properties

Melting temperature (10°C/min)
200
°C
Glass transition temperature (10°C/min)
58
°C
Temp. of deflection under load (1.80 MPa)
153
°C
Temp. of deflection under load (0.45 MPa)
184
°C

Other properties

Density
1170
kg/m³

Material specific properties

Tensile modulus (3D printed: flat X-X direction)
7630
MPa
Stress at yield (3D printed: flat X-X direction)
110
MPa
Strain at yield (3D printed: flat X-X direction)
2.5
%
Stress at break (3D printed: flat X-X direction)
110
MPa
Strain at break (3D printed: flat X-X direction)
2.2
%
Tensile modulus (3D printed: flat Y-X direction)
2720
MPa
Stress at yield (3D printed: flat Y-X direction)
63
MPa
Strain at yield (3D printed: flat Y-X direction)
3
%
Stress at break (3D printed: flat Y-X direction)
58
MPa
Strain at break (3D printed: flat Y-X direction)
4.5
%