Novamid® 1010C2

Injection Molding, High Flow, Easy Molding Grade, Lubricated, Nucleated

General Information

Novamid® is a high-quality polyamide, that has been developed as a special product line in order to cope with high demand levels from our Japanese customers.
Novamid® has seen various applications in various fields and various regions. From car to packaging, Novamid® is supported by an experienced and wide range of experts.
Product
Good and fast flow-ability. Easy mold release. Smooth surface appearance. Ideal for injection molding.
Special features
Regulatory Affairs
Processing technology
Injection Molding

Rheological properties

Melt volume-flow rate
56
cm³/10min
Temperature
230
°C
Load
2.16
kg
Melt flow index MFI
56
g/10min
MFI test temperature
230
°C
MFI test load
2.16
kg
Molding shrinkage [parallel]
1.2
%
Molding shrinkage [normal]
1.3
%

Mechanical properties

Tensile modulus
3100
MPa
Yield stress
85
MPa
Yield strain
4.2
%
Nominal strain at break
18
%
Flexural modulus
2800
MPa
Flexural strength
102
MPa
Charpy impact strength (+23°C)
N
kJ/m²
Charpy notched impact strength (+23°C)
4.2
kJ/m²

Thermal properties

Melting temperature (10°C/min)
220
°C
Temp. of deflection under load (1.80 MPa)
61
°C
Temp. of deflection under load (0.45 MPa)
150
°C
Coeff. of linear therm. expansion (parallel)
0.7
E-4/°C
Coeff. of linear therm. expansion (normal)
0.8
E-4/°C
Burning Behav. at thickness h
V-2
class
Thickness tested
0.81
mm
UL recognition
Yes
-
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (1) tested)
0.8
mm
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (2) tested)
3
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
0.81
mm
Relative Temperature Index - with impact
75
°C
RTI with impact (Thickness (2) tested)
3
mm
Relative Temperature Index - without impact
80
°C
RTI without impact (Thickness (1) tested)
0.81
mm
Relative Temperature Index - without impact
85
°C
RTI without impact (Thickness (2) tested)
3
mm

Electrical properties

Relative permittivity (100Hz)
4
-
Relative permittivity (1 MHz)
4
-
Dissipation factor (100 Hz)
110
E-4
Dissipation factor (1 MHz)
230
E-4
Volume resistivity
>1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
27
kV/mm
Comparative tracking index
600
V

Other properties

Humidity absorption
2.8
%
Density
1130
kg/m³

Material specific properties

Viscosity number
118
cm³/g