ForTii® MX2

40% Glass Reinforced, PA4T, Heat Stabilized, for Automotive applications

Back to results

General Information

ForTii® is a breakthrough high temperature polyamide with halogen-free and halogen containing flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want – and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
Product

ForTii® MX2 is a high Tg PPA that outperforms in dimensional stability at elevated temperatures due to the high heat deflection temperature (HDT). MX2 has excellent fatigue performance and good chemical resistance.

Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-04-25
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Processing technology
Injection Molding
Design challenge
Designing structural parts | CAE
Designing structural parts | high strength and stiffness solutions
Automotive OEM
CALLOUT, JAGUAR LAND ROVER
OEM Specification
ASTM D6779 PA152G40
STJLR.51.5262-(2018-02)
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.35
%
Molding shrinkage (normal)
1
%
Spiral flow length 1.0 mm 1000 bar
82
mm

Mechanical properties

Tensile modulus
14500
MPa
Tensile modulus (-40°C)
14800
MPa
Tensile modulus (40°C)
14200
MPa
Tensile modulus (80°C)
13500
MPa
Tensile modulus (100°C)
12800
MPa
Tensile modulus (120°C)
9500
MPa
Tensile modulus (150°C)
6700
MPa
Tensile modulus (160°C)
6300
MPa
Tensile modulus (180°C)
5500
MPa
Tensile modulus (200°C)
5300
MPa
Tensile modulus (210°C)
5000
MPa
Stress at break
230
MPa
Stress at break (-40°C)
250
MPa
Stress at break (40°C)
220
MPa
Stress at break (80°C)
200
MPa
Stress at break (100°C)
170
MPa
Stress at break (120°C)
140
MPa
Stress at break (150°C)
105
MPa
Stress at break (160°C)
95
MPa
Stress at break (180°C)
85
MPa
Stress at break (200°C)
78
MPa
Stress at break (210°C)
73
MPa
Strain at break
2.3
%
Strain at break (-40°C)
2.2
%
Strain at break (40°C)
2.2
%
Strain at break (80°C)
2.5
%
Strain at break (100°C)
3
%
Strain at break (120°C)
5.1
%
Strain at break (150°C)
6.9
%
Strain at break (160°C)
7
%
Strain at break (180°C)
7
%
Strain at break (200°C)
7
%
Strain at break (210°C)
7
%
Flexural modulus
14000
MPa
Flexural modulus (120°C)
9800
MPa
Flexural modulus (160°C)
6000
MPa
Flexural modulus (180°C)
5400
MPa
Flexural modulus (200°C)
5000
MPa
Flexural modulus (210°C)
4900
MPa
Flexural strength
350
MPa
Flexural strength (120°C)
200
MPa
Flexural strength (160°C)
140
MPa
Flexural strength (180°C)
110
MPa
Flexural strength (200°C)
100
MPa
Flexural strength (210°C)
95
MPa
Charpy impact strength (+23°C)
70
kJ/m²
Charpy impact strength (-30°C)
65
kJ/m²
Charpy notched impact strength (+23°C)
11
kJ/m²
Charpy notched impact strength (-30°C)
10
kJ/m²
Weldline strength at thickness 1
85
MPa
Weldline strain at thickness 1
0.8
%
Thickness tested (1)
4
mm

Thermal properties

Melting temperature (10°C/min)
325
°C
Glass transition temperature (10°C/min)
125
°C
Glass Transition Temperature from DMTA (tan d)
130
°C
Temp. of deflection under load (1.80 MPa)
305
°C
Temp. of deflection under load (0.45 MPa)
317
°C
Coeff. of linear therm. expansion (parallel)
0.17
E-4/°C
Coeff. of linear therm. expansion (normal)
0.55
E-4/°C
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
Coeff. of linear therm. expansion (normal)
0.35
E-4/°C
Glow Wire Flammability Index GWFI
725
°C
GWFI (Thickness (1) tested)
0.8
mm
Glow Wire Flammability Index GWFI
700
°C
GWFI (Thickness (2) tested)
1.5
mm
Glow Wire Ignition Temperature GWIT
725
°C
GWIT (Thickness (1) tested)
0.8
mm
Glow Wire Ignition Temperature GWIT
725
°C
GWIT (Thickness (2) tested)
1.5
mm
Thermal Index 2500 hrs
188
°C
Thermal Index 5000 hrs
175
°C
Thermal Index 10000 hrs
164
°C
Thermal Index 20000 hrs
153
°C

Electrical properties

Relative permittivity (100Hz)
4.9
-
Relative permittivity (1 MHz)
4.6
-
Dissipation factor (100 Hz)
57
E-4
Dissipation factor (1 MHz)
180
E-4
Volume resistivity
>1E13
Ohm*m
Surface resistivity
Ohm

Other properties

Water absorption
4.7
%
Water absorption in water at 23°C after 24h
0.35
%
Humidity absorption
1.8
%
Density
1550
kg/m³

Diagrams

Applications

Crankshaft Covers

Industry
Automotive
Material
  • •} Suitable for strict chemical or dimensional stability requirements
  • •} Cost effective
  • •} Heat resistant
  • •} Creep resistant
  • •} Oil resistant
  • •} Fatigue resistant
  • •} Lightweight
}
More information