EcoPaXX® Q210E-H
High Viscosity, Heat Stabilized, Food Contact Quality
General Information
EcoPaXX® is our bio-based, high-performance polyamide (PA410) that offers outstanding performance across the board, while being made mainly from tropical castor beans which don’t compete with the food chain.
EcoPaXX® belongs to the family of long-chain polyamides, which offer exceptional performance in the most demanding of environments. That includes excellent chemical resistance, low moisture absorption, combined with a very high melting point (highest of all bio-plastics) and high crystallization rate (typical for engineering plastics like PA66 and PA46).
EcoPaXX® has the lowest carbon footprint amongst common polyamides. This is because the amount of carbon dioxide emitted during the production of EcoPaXX® is offset by the amount absorbed in plant growth, and in particular by the riccinus communis – the tropical castor bean plant that makes up some 70% of EcoPaXX®. Externally certified lifecycle analysis (LCA) data is available upon request.
Product
EcoPaXX® Q210E-H is a high viscous long aliphatic polyamide which offers excellent wear & friction properties at high humidity for use in gears, food conveyer belt parts and abrasive monofilaments.
EcoPaXX® Q210E-H is a high viscous long aliphatic polyamide which offers excellent wear & friction properties at high humidity for use in gears, food conveyer belt parts and abrasive monofilaments.
Sustainability
Bio-based
Bio-based
Special features
- Heat stabilized
- High viscosity
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration Biocidal Products2023-11-16
- Absence Declaration EPA 20 High Priority Substances 20192023-11-16
- Absence Declaration Food Allergens2023-11-16
- Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-03-21
- Food Contact Canada Information (LONO)2019-07-08
- Food Contact Declaration Europe EcoPaXX®2023-08-10
- Food Contact Declaration USA EcoPaXX®2023-11-21
- Food Contact India Information Letter2023-05-11
- Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
- REACH Registration Statement2024-03-27
- REACH STATEMENT KOREA2023-11-16
- REACH STATEMENT TURKYE2023-11-16
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-03-27
- Turkish customs legislation info letter (EK-8 form)2023-11-16
Processing technology
Extrusion, Injection Molding
Extrusion, Injection Molding
Design challenge
Life cycle assessment
Life cycle assessment
Automotive OEM
HYUNDAI KIA
HYUNDAI KIA
OEM Specification
MS-211-66-(2018)
MS-211-66-(2018)
Applications
Rheological properties
Melt volume-flow rate
8.5
cm³/10min
ISO 1133
Temperature
280
°C
ISO 1133
Load
2.16
kg
ISO 1133
Melt flow index MFI
8
g/10min
ISO 1133
MFI test temperature
280
°C
ISO 1133
MFI test load
2.16
kg
ISO 1133
Molding shrinkage (parallel)
2.4
%
ISO 294-4
Molding shrinkage (normal)
1.6
%
ISO 294-4
Mechanical properties
Tensile modulus
3000
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
3300
MPa
ISO 527-1/-2
Tensile modulus (40°C)
2800
MPa
ISO 527-1/-2
Tensile modulus (80°C)
800
MPa
ISO 527-1/-2
Tensile modulus (100°C)
650
MPa
ISO 527-1/-2
Tensile modulus (120°C)
600
MPa
ISO 527-1/-2
Tensile modulus (140°C)
460
MPa
ISO 527-1/-2
Yield stress
85
MPa
ISO 527-1/-2
Yield stress (-40°C)
115
MPa
ISO 527-1/-2
Yield stress (100°C)
35
MPa
ISO 527-1/-2
Yield strain
4.4
%
ISO 527-1/-2
Yield strain (-40°C)
8
%
ISO 527-1/-2
Nominal strain at break
20
%
ISO 527-1/-2
Nominal strain at break (-40°C)
12
%
ISO 527-1/-2
Nominal strain at break (100°C)
>50
%
ISO 527-1/-2
Nominal strain at break (120°C)
>50
%
ISO 527-1/-2
Flexural modulus
2850
MPa
ISO 178
Flexural modulus (120°C)
500
MPa
ISO 178
Flexural strength
115
MPa
ISO 178
Flexural strength (120°C)
18
MPa
ISO 178
Charpy impact strength (+23°C)
N
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
N
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
4.5
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
4.5
kJ/m²
ISO 179/1eA
Weldline strength at thickness 1
85
MPa
ISO 527-1/-2
Weldline strain at thickness 1
24
%
ISO 527-1/-2
Thickness tested (1)
4
mm
ISO 527-1/-2
Thermal properties
Melting temperature (10°C/min)
250
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
77
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
175
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.9
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.8
E-4/°C
ISO 11359-1/-2
Oxygen index
24
%
ISO 4589-1/-2
Thermal Index 2500 hrs
153
°C
IEC 60216/ISO 527-1/-2
Thermal Index 5000 hrs
144
°C
IEC 60216/ISO 527-1/-2
Thermal Index 10000 hrs
135
°C
IEC 60216/ISO 527-1/-2
Other properties
Water absorption
5.8
%
Sim. to ISO 62
Humidity absorption
2.1
%
Sim. to ISO 62
Density
1090
kg/m³
ISO 1183
Material specific properties
Viscosity number
210
cm³/g
ISO 307, 1157, 1628
Diagrams
Applications
Abrasive brush monofilament
Industry
Consumer goods
Material
- •} Heat-stabilized
- •} High viscosity
- •} Bio-based (nearly 70% is made from the tropical castor bean plant)
- •} Low carbon footprint (CO₂ emitted during production offset by CO₂ absorbed by plant growth)
- •} Processed through extrusion or injection molding.