Arnite® TV4 251 XG2

25% Glass Reinforced, Flame Retardant (halogen free)

Back to results

General Information

Arnite® T (PBT) is a high-performance engineering plastic that combines high strength and rigidity with excellent processing characteristics. It’s well suited for a broad range of automotive, electrical & electronic and consumer goods applications.
Special features
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2023-11-16
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • CALIFORNIA PROPOSITION 65 (INDUSTRIAL USE)2024-01-02
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Yellow Card
Processing technology
Injection Molding
Applications
Have a question? Contact us

Rheological properties

Melt volume-flow rate
18
cm³/10min
Temperature
270
°C
Load
2.16
kg
Molding shrinkage [parallel]
0.7
%
Molding shrinkage [normal]
1.3
%

Mechanical properties

Tensile modulus
8500
MPa
Stress at break
95
MPa
Strain at break
2
%
Charpy impact strength (+23°C)
30
kJ/m²
Charpy impact strength (-30°C)
30
kJ/m²
Charpy notched impact strength (+23°C)
5
kJ/m²
Charpy notched impact strength (-30°C)
5
kJ/m²

Thermal properties

Melting temperature (10°C/min)
225
°C
Temp. of deflection under load (1.80 MPa)
210
°C
Temp. of deflection under load (0.45 MPa)
220
°C
Burning Behav. at 1.5 mm nom. thickn.
V-2
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Ball pressure temperature
215
°C
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (1) tested)
0.75
mm
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (2) tested)
1.5
mm
Relative Temperature Index - electrical
140
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - electrical
140
°C
RTI electrical (Thickness (2) tested)
1.6
mm
Relative Temperature Index - with impact
130
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
130
°C
RTI with impact (Thickness (2) tested)
1.6
mm
Relative Temperature Index - without impact
140
°C
RTI without impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - without impact
140
°C
RTI without impact (Thickness (2) tested)
1.6
mm

Electrical properties

Comparative tracking index
550
V
Comparative tracking index (PLC)
1
class

Other properties

Water absorption
0.3
%
Humidity absorption
0.15
%
Density
1540
kg/m³

Diagrams

Applications

Motor Starter/Overload Relays

Industry
Electrical
Material
Most grades are available with halogenfree flameretardancy, and in specific electro-grey colour for housings. Also Lasermarkable grades are available. ForTii® has a Heat Deflection Temperature (HDT) of 305°C .}
More information

Residual Current Breaker with Overload

Industry
Electrical
Material
Most grades are available with halogenfree flameretardancy, and in specific electro-grey colour for housings.}
More information