Akulon® Diablo HT-HG0

50% Glass Reinforced, Heat Stabilized

Back to results

General Information

Akulon® is our family of high performance polyamide 6 and polyamide 66 materials, used by customers across the world in applications ranging from automotive, electronics & electrical, to furniture and packaging.
We offer Akulon® grades for injection molding, blow molding and extrusion (including barrier film, stock shapes, convoluted tubes, and mono and multi filament).
In molded parts the material offers an excellent balance of easy design and processing with outstanding mechanical properties over a wide temperature range and in diverse conditions. Meanwhile for extrusion the strength, resilience and easy processing of Akulon® sets the market standards.
Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-04-25
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-03-21
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
  • Turkish customs legislation info letter (EK-8 form)2023-11-16
Processing technology
Injection Molding
Design challenge
Degradation & Stability | Thermo-oxidative stability
Designing structural parts | high strength and stiffness solutions
Automotive OEM
CALLOUT, RENAULT
OEM Specification
ASTM D6779 PA0820A64490 (9=245)
PMR (2019-02)
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.3
%
Molding shrinkage (normal)
1
%

Mechanical properties

Tensile modulus
16500
MPa
Tensile modulus (-40°C)
17000
MPa
Tensile modulus (40°C)
15000
MPa
Tensile modulus (100°C)
7100
MPa
Tensile modulus (120°C)
6700
MPa
Tensile modulus (150°C)
5600
MPa
Tensile modulus (180°C)
4650
MPa
Tensile modulus (200°C)
4100
MPa
Stress at break
235
MPa
Stress at break (-40°C)
300
MPa
Stress at break (100°C)
120
MPa
Stress at break (120°C)
105
MPa
Stress at break (150°C)
90
MPa
Stress at break (160°C)
85
MPa
Stress at break (180°C)
70
MPa
Stress at break (200°C)
60
MPa
Strain at break
2.8
%
Strain at break (-40°C)
2.6
%
Strain at break (120°C)
6.7
%
Strain at break (150°C)
6.9
%
Strain at break (160°C)
7
%
Strain at break (180°C)
7.1
%
Strain at break (200°C)
7.2
%
Flexural modulus
16000
MPa
Flexural modulus (120°C)
7300
MPa
Flexural modulus (160°C)
6500
MPa
Flexural modulus (180°C)
5800
MPa
Flexural modulus (200°C)
5250
MPa
Flexural modulus (210°C)
4900
MPa
Flexural strength
360
MPa
Flexural strength (120°C)
150
MPa
Flexural strength (160°C)
120
MPa
Flexural strength (180°C)
108
MPa
Flexural strength (200°C)
87
MPa
Flexural strength (210°C)
80
MPa
Charpy impact strength (+23°C)
95
kJ/m²
Charpy impact strength (-30°C)
80
kJ/m²
Charpy notched impact strength (+23°C)
15.5
kJ/m²
Charpy notched impact strength (-30°C)
14
kJ/m²
Weldline strength at thickness 1
90
MPa
Weldline strain at thickness 1
0.9
%
Thickness tested (1)
4
mm

Thermal properties

Melting temperature (10°C/min)
260
°C
Temp. of deflection under load (1.80 MPa)
245
°C
Temp. of deflection under load (0.45 MPa)
255
°C

Other properties

Water absorption
4.8
%
Water absorption in water at 23°C after 24h
1.8
%
Humidity absorption
1.7
%
Density
1580
kg/m³

Diagrams

Applications

Charge Air Cooler Caps

Industry
Automotive
Material
  • •} Long term heat resistant
  • •} Lightweight
  • •} Cost effective
  • •} Fatigue resistant
}
More information

Integrated Air Inlet Manifolds (up to 180°C)

Industry
Automotive
Material
  • •} Long-term heat resistance up to 230 C
  • •} Lower system costs compared to metal.
}
More information

Resonators and ByPass Valves

Industry
Automotive
Material
  • •} Lightweight
  • •} Economical
  • •} Reliable
  • •} Durable
  • •} Heat
resistant
  • •} Chemical resistant
}
More information