Akulon® Diablo HDT2500, (PA66+PA6)-GF35 - Envalior

Akulon® Diablo HDT2500

35% Glass Reinforced, Heat Stabilized

General Information

Akulon® is our family of high performance polyamide 6 and polyamide 66 materials, used by customers across the world in applications ranging from automotive, electronics & electrical, to furniture and packaging.

We offer Akulon® grades for injection molding, blow molding and extrusion (including barrier film, stock shapes, convoluted tubes, and mono and multi filament).

In molded parts the material offers an excellent balance of easy design and processing with outstanding mechanical properties over a wide temperature range and in diverse conditions. Meanwhile for extrusion the strength, resilience and easy processing of Akulon® sets the market standards.

Special features

Heat stabilized

General Document

Regulatory Affairs

Absence Declaration BNST2023-11-16
Absence Declaration Biocidal Products2023-11-16
Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
Absence Declaration EPA 20 High Priority Substances 20192023-11-16
Absence Declaration Food Allergens2023-11-16
Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
Absence Declaration Nano Materials2023-11-16
Absence Declaration Ozone Depleting Chemicals2024-04-25
Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
Absence Declaration PFAS2024-03-05
Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
Absence Declaration Red Phosphorus2023-11-16
Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
Conflict minerals declaration (EICC, GeSI)2024-03-21
Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
REACH Registration Statement2024-03-27
REACH STATEMENT KOREA2023-11-16
REACH STATEMENT TURKYE2023-11-16
RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Turkish customs legislation info letter (EK-8 form)2023-11-16

Processing technology
Injection Molding

Design challenge
Degradation & Stability | Thermo-oxidative stability

Automotive OEM
FIAT CHRYSLER, PSA, RENAULT

OEM Specification
01994-15-00281-(2017-12)
FCA-MS50017(MS-DB-41)-CPN5077-(2017-02)
PMR (2019-02)
STELLANTIS - 01994-16-00164-MAN-01994-15-00281-(2021-07)

Rheological properties

Molding shrinkage (parallel)

0.3

ISO 294-4

Molding shrinkage (normal)

0.9

ISO 294-4

Mechanical properties

Tensile modulus

11000

MPa

ISO 527-1/-2

Tensile modulus (-40°C)

11300

MPa

ISO 527-1/-2

Tensile modulus (40°C)

10200

MPa

ISO 527-1/-2

Tensile modulus (100°C)

5100

MPa

ISO 527-1/-2

Tensile modulus (120°C)

4500

MPa

ISO 527-1/-2

Tensile modulus (150°C)

4200

MPa

ISO 527-1/-2

Tensile modulus (160°C)

4100

MPa

ISO 527-1/-2

Tensile modulus (180°C)

3800

MPa

ISO 527-1/-2

Tensile modulus (200°C)

3200

MPa

ISO 527-1/-2

Tensile modulus (210°C)

2800

MPa

ISO 527-1/-2

Stress at break

195

MPa

ISO 527-1/-2

Stress at break (-40°C)

255

MPa

ISO 527-1/-2

Stress at break (100°C)

105

MPa

ISO 527-1/-2

Stress at break (120°C)

MPa

ISO 527-1/-2

Stress at break (150°C)

MPa

ISO 527-1/-2

Stress at break (160°C)

MPa

ISO 527-1/-2

Stress at break (180°C)

MPa

ISO 527-1/-2

Stress at break (200°C)

MPa

ISO 527-1/-2

Stress at break (210°C)

MPa

ISO 527-1/-2

Strain at break

3.2

ISO 527-1/-2

Strain at break (-40°C)

3.2

ISO 527-1/-2

Strain at break (120°C)

9.2

ISO 527-1/-2

Strain at break (150°C)

9.6

ISO 527-1/-2

Strain at break (160°C)

9.6

ISO 527-1/-2

Strain at break (180°C)

9.6

ISO 527-1/-2

Strain at break (200°C)

9.6

ISO 527-1/-2

Strain at break (210°C)

ISO 527-1/-2

Flexural modulus

10500

MPa

ISO 178

Flexural modulus (120°C)

4600

MPa

ISO 178

Flexural modulus (160°C)

4200

MPa

ISO 178

Flexural modulus (180°C)

4000

MPa

ISO 178

Flexural modulus (200°C)

3600

MPa

ISO 178

Flexural modulus (210°C)

3300

MPa

ISO 178

Flexural strength

290

MPa

ISO 178

Flexural strength (120°C)

130

MPa

ISO 178

Flexural strength (160°C)

105

MPa

ISO 178

Flexural strength (180°C)

MPa

ISO 178

Flexural strength (200°C)

MPa

ISO 178

Flexural strength (210°C)

MPa

ISO 178

Charpy impact strength (+23°C)

kJ/m²

ISO 179/1eU

Charpy impact strength (-30°C)

kJ/m²

ISO 179/1eU

Charpy notched impact strength (+23°C)

kJ/m²

ISO 179/1eA

Charpy notched impact strength (-30°C)

kJ/m²

ISO 179/1eA

Weldline strength at thickness 1

MPa

ISO 527-1/-2

Weldline strain at thickness 1

2.1

ISO 527-1/-2

Thickness tested (1)

ISO 527-1/-2

Thermal properties

Melting temperature (10°C/min)

260

°C

ISO 11357-1/-3

Temp. of deflection under load (1.80 MPa)

240

°C

ISO 75-1/-2

Temp. of deflection under load (0.45 MPa)

258

°C

ISO 75-1/-2

Coeff. of linear therm. expansion (parallel)

0.4

E-4/°C

ISO 11359-1/-2

Coeff. of linear therm. expansion (normal)

0.5

E-4/°C

ISO 11359-1/-2

Other properties

Water absorption

Sim. to ISO 62

Humidity absorption

2.1

Sim. to ISO 62

Density

1410

kg/m³

ISO 1183

Material specific properties

Viscosity number

135

cm³/g

ISO 307, 1157, 1628

Rheological calculation properties

Density of melt

1220

kg/m³

Thermal conductivity of melt

0.27

W/(m K)

Spec. heat capacity melt

2060

J/(kg K)