Stanyl® TW242FM10

Mit 50% Glasfasern/Mineral verstärkt, wärmestabilisiert

Allgemeine Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Besondere Merkmale
Regulatorische Angelegenheiten
Verarbeitung
Injection Molding

Rheologische Kennwerte

Verarbeitungsschwindung parallel
0.2
%
Verarbeitungsschwindung senkrecht
1.25
%
Spiralfliesslänge, 0.5mm 1200bar
32
mm
Spiralfliesslänge, 0.5mm 1600bar
48
mm
Spiralfliesslänge, 0.5mm 2000bar
60
mm

Mechanische Kennwerte

Zug-Modul
14500
MPa
Bruchspannung
160
MPa
Bruchdehnung
2
%
Biegemodul
11000
MPa
Biegefestigkeit
225
MPa
Charpy-Kerbschlagzähigkeit (+23°C)
6
kJ/m²
Charpy-Kerbschlagzähigkeit (-30°C)
4.5
kJ/m²
Izod-Kerbschlagzähigkeit (23°C)
6
kJ/m²
Izod-Kerbschlagzähigkeit (-40°C)
4
kJ/m²

Thermische Kennwerte

Schmelztemperatur (10°C/min)
295
°C
Glasübergangstemperatur (10°C/min)
75
°C
Formbeständigkeitstemperatur (1.8 MPa)
285
°C
Formbeständigkeitstemperatur (0.45 MPa)
290
°C
Längenausdehnungskoeffizient (parallel)
0.25
E-4/°C
Längenausdehnungskoeffizient (senkrecht)
0.5
E-4/°C

Sonstige Kennwerte

Wasseraufnahme
6.75
%
Wasseraufnahme in Wasser bei 23°C nach 24h
1.9
%
Feuchtigkeitsaufnahme
1.8
%
Dichte
1630
kg/m³

Rheologische Berechnungsparameter

Dichte der Schmelze
1430
kg/m³
Wärmeleitfähigkeit der Schmelze
0.391
W/(m K)
Spez. Wärmekapazität der Schmelze
1680
J/(kg K)
Effektive Temperaturleitf. a-effektiv
1.64E-7
m²/s