Stanyl® HFX33S

Mit 20% Glasfasern verstärkt, sehr gute Fließfähigkeit, Frei von rotem Phosphor und Halogenen

Allgemeine Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Produkt
Stanyl® HFX33S is an electro-friendly & halogen-free flame-retarded high heat polyamide that offers an excellent combination of high CTI, flow and weld-line strength. HFX-grades are often used in connectors such as USB type C.
Besondere Merkmale
Regulatorische Angelegenheiten
Verarbeitung
Injection Molding
Designanforderung
Downsizing & Miniaturization
Flame Retardancy | Halogen free

Rheologische Kennwerte

Verarbeitungsschwindung parallel
0.4
%
Verarbeitungsschwindung senkrecht
1.5
%
Spiralfliesslänge, 1.0 mm 800bar
165
mm
Spiralfliesslänge, 1.0 mm 900bar
180
mm
Spiralfliesslänge, 1.0 mm 1000bar
200
mm

Mechanische Kennwerte

Zug-Modul
7700
MPa
Bruchspannung
115
MPa
Bruchdehnung
2.7
%
Biegemodul
7000
MPa
Biegefestigkeit
170
MPa
Charpy-Kerbschlagzähigkeit (+23°C)
6.5
kJ/m²

Thermische Kennwerte

Schmelztemperatur (10°C/min)
295
°C
Glasübergangstemperatur (10°C/min)
75
°C
Formbeständigkeitstemperatur (1.8 MPa)
276
°C
Formbeständigkeitstemperatur (0.45 MPa)
284
°C
Brennbarkeit bei nominal 1.5mm
V-0
class
geprüfte Probekörperdicke
3
mm
UL Registrierung
Yes
-
Brennbarkeit bei Dicke h
V-0
class
geprüfte Probekörperdicke
0.4
mm
UL Registrierung
Yes
-

Elektrische Kennwerte

Dielektrizitätszahl (1GHz)
3.5
-
Dielektr. Verlustfaktor (1GHz)
100
E-4
Elektrische Durchschlagfestigkeit
30
kV/mm
Vergleichszahl der Kriechwegbildung
500
V

Sonstige Kennwerte

Dichte
1370
kg/m³

Diagramme

Anwendungsbeispiele

USB-C Connectors

Branche
Electronics
  • <ul> <li>Stanyl® PA46 offers the safest solution for USB connectors due to high HDT's a CTI rating of 600V is achieved (enabling up to 27 Watt power). The high CTI Stanyl® fails only after more than 2x the number of salt solution droplets compared to a lower CTI LCP during CTI (Comparative Tracking Index) test.</li> <li>Due to the high wear resistance Stanyl® PA46 shows no sign of wear after 10,000 insertion/extraction cycles, where a PA9T shows a clear wear out at the mating surface after durability tests.</li> <li>Stanyl® PA46 allow for cost effective solutions due to its excellent processability and high flowability, enabling thin walled designs and strong weld lines. Stanyl PA46’s weld line strength is 3 times higher than that of a LCP or PA9T.</li> <li>UL94-V0 at 0.2mm wall thickness, extensive color portfolio, including light colors. No blistering in USB-C connector designs.</li> <li>Stanyl® PA46 powers high-bandwidth USB-C connectors for Virtual Reality - Virtual Link Connectors (SuperSpeed USB 10Gbps) for headset cameras and sensors.</li> </ul>